Search for: All records

Unbiased photoelectrochemical hydrogen production with high efficiency and durability is highly desired for solar energy storage. Here, we report a microbial photoelectrochemical (MPEC) system that demonstrated superior performance when equipped with bioanodes and black silicon photocathode with a unique “Swiss-cheese” interface. The MPEC utilizes the chemical energy embedded in wastewater organics to boost solar H 2 production, which overcomes barriers on anode H 2 O oxidation. Without any bias, the MPEC generates a record photocurrent (up to 23 mA cm −2 ) and retains prolonged stability for over 90 hours with high Faradaic efficiency (96–99%). The calculated turnover number for MoS x catalyst during a 90 h period is 495 471 with an average frequency of 1.53 s −1 . The system replaced pure water on the anode with actual wastewater and achieved waste organic removal up to 16 kg COD m −2 photocathode per day. Cost credits from concurrent wastewater treatment and low-cost design make photoelectrochemical H 2 production practical for the first time. 

2D early transition metal carbide and nitride MXenes have intriguing properties for electrochemical energy storage and electrocatalysis. These properties can be manipulated by modifying the basal plane chemistry. Here, mixed transition metal nitride MXenes, M‐Ti₄N₃T_x(M = V, Cr, Mo, or Mn; T_x= O and/or OH), are developed by modifying pristine exfoliated Ti₄N₃T_xMXene with V, Cr, Mo, and Mn salts using a simple solution‐based method. The resulting mixed transition metal nitride MXenes contain 6–51% metal loading (cf. Ti) that exhibit rich electrochemistry including highly tunable hydrogen evolution reaction (HER) electrocatalytic activity in a 0.5mH₂SO₄electrolyte as follows: V‐Ti₄N₃T_x> Cr‐Ti₄N₃T_x> Mo‐Ti₄N₃T_x> Mn‐Ti₄N₃T_x> pristine Ti₄N₃T_xwith overpotentials as low as 330 mV at −10 mA cm⁻²with a charge‐transfer resistance of 70 Ω. Scanning electrochemical microscopy (SECM) reveals the electrochemical activity of individual MXene flakes. The SECM data corroborate the bulk HER activity trend for M‐Ti₄N₃T_xas well as provide the first experimental evidence that HER results from catalysis on the MXene basal plane. These electrocatalytic results demonstrate a new pathway to tune the electrochemical properties of MXenes for water splitting and related electrochemical applications.

 

Herein, antimony sulfoselenide (Sb₂(S, Se)₃) thin‐film solar cells are fabricated by a hydrothermal method followed by a post‐deposition annealing process at different temperatures and the impact of the annealing temperature on the morphological, structural, optoelectronic, and defect properties of the hydrothermally grown Sb₂(S, Se)₃films is investigated. It is found that a proper annealing temperature leads to high‐quality Sb₂(S, Se)₃films with large crystal grains, high crystallinity, preferred crystal orientation, smooth and uniform morphology, and reduced defect density. These results show that suppressing deep‐level defects is crucial to enhance solar cell performance. After optimizing the annealing process, Sb₂(S, Se)₃solar cells with an improved power conversion efficiency 2.04 to 8.48% are obtained.

 

Maximizing the power conversion efficiency (PCE) of perovskite/silicon tandem solar cells that can exceed the Shockley-Queisser single-cell limit requires a high-performing, stable perovskite top cell with a wide bandgap. We developed a stable perovskite solar cell with a bandgap of ~1.7 electron volts that retained more than 80% of its initial PCE of 20.7% after 1000 hours of continuous illumination. Anion engineering of phenethylammonium-based two-dimensional (2D) additives was critical for controlling the structural and electrical properties of the 2D passivation layers based on a lead iodide framework. The high PCE of 26.7% of a monolithic two-terminal wide-bandgap perovskite/silicon tandem solar cell was made possible by the ideal combination of spectral responses of the top and bottom cells.